a crack in the glass that occurs only on the inside lite of the window that is usually caused by a rapid change in temperature
External or internal cracks in a composite caused by tensile stresses; cracking can be present internally, externally or in combination.
External or internal crack in a composite caused by tensile stresses; cracking may be present internally, externally or in combination.
A crack in piping or other component caused by age or abnormal conditions such as vibration.
External or internal cracks in a plastic caused by tensile stresses; often appear as a network of fine cracks known as crazing.
A crack, either external or internal, in a plastic caused by tensile stresses less than its short-time mechanical strength.
An external or internal crack in a plastic caused by tensile stresses less than its short-time mechanical strength.
An internal or external crack that results from tensile stresses lower than the short-time mechanical strength.
A crack in the glass of an Insulated Unit caused by excessive heat or cold. Excessive heat can build up in the air space between the glass causing the air to expand and the glass to break.
An external or internal crack in the plastic caused by tensile stress less than that of its short-time mechanical strength. The development of such cracks is frequently accelerated by the environment to which the plastic is exposed. The stresses which cause cracking may be present internally or externally or may be combinations of these stresses. The appearance of a network of fine cracks is crazing.
(1) Cracks in plaster and drywall caused by heat or moisture expansion. (2) Cracks in plaster and drywall caused by building stress due to expansion and contraction.
external or internal cracks within a material caused by long-term stress.
External or internal crack in a plastic caused by tensile stresses. The development of such cracks is frequently accelerated by the environment to which the plastic is exposed. The stresses that cause cracking may be present internally or externally or a combination of both. Apperance of a network of fine cracks is called crazing.